The Effect of Preheating and Non-Preheating in Cast Iron Welding Toward Mechanical Properties
DOI:
https://doi.org/10.24036/teknomekanik.v3i2.7272Keywords:
Effect of Welding, Preheating, Cast iron, Bending Test, SMAWAbstract
Cast iron material is a material that has brittle properties and is less able to withstand stress due to the welding cycle caused by flake graphite in cast iron. Because of these problems, in connecting cast iron materials using the SMAW welding method, it is necessary to have heat treatment (preheating) to avoid the welding problems on the properties of cast iron. The purpose of this study is to determine the effect of heating and non-heating on the cast iron before the welding process. Therefore, this research will play a crucial contribution as a reference for cast iron welding researchers and cast iron welding process. The method of the research was experimental research, where the measurement results were obtained directly from the specimens. The welding was using an open V seam. The specimen used was cast iron with a thickness of 8 mm. One cast iron was given heat treatment at a temperature of 260ºC and the others did not receive heat treatment before being welded. The welding process used SMAW with CIN - 2 electrodes with a diameter of 3 mm. The test used the bending test on the face specimens according to the American Welding Society D1.1 standard. The results showed that there was an effect of the preheating treatment on cast iron, which that the non-preheating specimens were easier to fracture than the preheating specimens. Thus, it can be concluded that welding with preheating is better than welding without preheating.
Downloads
References
Cary, H.B, . Modern Welding Technology. 4 th Ed. New Jersey: Prentice Hall, 1998
Trihutomo, P. The Effect of Annealing Process on the welding results on the mechanical properties of low carbon steel. Journal of Mechanical Engineering: 2014: 1: 84-88.
A. Hamid, Analisa Pengaruh Arus Pengelasan SMAW Pada Material Baja Karbon Rendah Terhadap Kekuatan Material Hasil Sambungan, Jurnal Teknik Elektro: 2016: 7 (1); 26–36.
D. Patel, S. Patel, J. Parekh, and S. Chaudhary, A Review on Effect of Different Process Parameters of SMAW, Implementation Journal Interdiscip: 2017; 3 (1); 1384–1389.
Konecna R. Nicoletto G. Bubenko L. Fintova S. A Comparative Study of the fatigue behavior of two heat-treated nodular cast iron. Enginering Fracture Mechanics: 2013: 108-256. Doi 10.1016/j.engfracmech.2013.04.017.
Dieter, George E. Metalurgi Mekanik, Jakarta: Erlangga. 1996.
Daryanto. Teknik Las. Bandung: Alfabeta. 2012.
Bodude, MA. Momohjimoh, I. Studies on Effects of Welding Parameters on the Mechanical. 2015.
Wiryosumarto. Teknologi Pengelasan Logam, Jakarta: Pradnya Paramita. 1991.
J. Verma and R. V. Taiwade. Effect of welding processes and conditions on the microstructure, mechanical properties and corrosion resistance of duplex stainless-steel weldments—A review. Journal of Manufacturing Processes. 2017; 25: 134-152.
S. Hestukoro, I. Roza, And D. Morfi Nst, Process Analysis Of High Speed Steel Cutting Calculation (HSS) With S45 C Material On Universal Machine Tool. Internatioanal Journal of Innovation. 2018: 3 (1). doi.org/10.24036/tm.v3i1.5572.
Nusulul Huda, Jasman, Pengaruh Kuat Arus Terhadap Uji Tarik Material Baja Karbon Rendah. . Ranah Research. 2019. 2 (1)
Daryanto. Keselamatan Dan Kesehatan Kerja Bengkel. Jakarta: Rineka Cipta. 2007.
Jariyaboon, M., Davenport, A.J., Ambat, R., Connolly, B.J., Williams, S.W., Price, D.A. The effect of welding parameters on the corrosion behaviour of friction stir welded AA2024-T351, Corrosion Science. 2007: 49 (2): 877-909. doi: 10.1016/j.corsci.2006.05.038.
Erizon, N. The effect of welding heat on low carbon steel on physical and mechanical. Ivotek. 2009; 10: 2359-2381.
Kenyon, W. Dasar-dasar Pengelasan, Jakarta: Erlangga. 1984.
Widharto, S. Welding Inspection, Mitra Wacana Media, Jakara. 2013.
A. V. Adedayo, S. A. Ibitoye And O. A. Oyetoyan, Annealing Heat Treatment Effects On Steel Welds; Journal Of Minerals And Materials Characterization And Engineering. 2010: 9 (9): 547-557.
Talabi, S.I.A, Owolabi, O.B.Effect Of Welding Variables On Mechanical Properties Of Low Carbon Steel Welded Joint. Journal Of Advances In Production Engineering & Management. 2013: 9 (4): 181-186. Doi.Org/10.14743/Apem2014.4.186, 2013.
Kenyon, W. Dasar-dasar Pengelasan, Jakarta: Erlangga. 1984.
Karadeniz, E., Ozsarac, U., Yildiz, C. The Effect Of Process Parameters On Penetration In Gas Metal Arc Welding Processes, Materials & Design. 2007: 28 (2): 649-656 Doi:10.1016/J.Matdes..07.014. 2005.
R. S. Funderburk. Key Concepts In Welding Engineering. Welding Innovation. 1997: Vol. XIV, no. 2.
Despa, Wandri, Purwantono, W. Pengaruh Arus AC dan DC Terhadap Hasil Pengelasan Pada Las Busur Listrik. Jurnal Pendidikan Teknik Mesin. 2016: 1–7.
Ferry Budhi Susetyo, Ja’far Amirudin, Studi Karakteristik Pengelasan Smaw Pada Baja Karbon
Rendah St 42 Dengan Elektroda E 7018. 1St Ed. Jakarta : Jurnal Konversi Energi Dan Manufaktur UNJ. 2013.
Sonawan, H., Suratman, R. Pengantar Untuk Memahami Pengelasan Logam, Bandung; Alfa Beta. 2004.
Jeffus, Larry. Welding: Principles and Application. Clifton Park, N. Y. : Delmar Cengage Learning. 2012.
S. Nutalapati, D. Azad, and G. S. Naidu, Effect of Welding Current on Welding Speed and Ultimate Tensile Strength (UTS) of Mild Steel, Internationl Journal Mechanical Enginering. 2016: 7 (5): 156–176.
M. Bin Afan, P. Purwantono, M. Mulianti, and B. Rahim, Pengaruh Suhu Penyimpanan Elektroda Low Hydrogen E7016 terhadap Hasil Uji Tekuk Sambungan Las Pelat Baja Karbon SS400, Jurnal Rekayasa Mesin. 2020: 15 (1): 20-25, doi:10.32497/jrm.v15i1.1823.
American Welding Society. Structural Welding Code-Steel. D1.1/D1.1M. 2015.